ZR230C

      AKSAD GROUP PETROCHEM

ZR230C

 

ZR230C is a high molecular weight Random Polypropylene copolymer for compression moulding and extrusion.

Product Description

ZR230C exhibits excellent heat resistance, and is designed to produce items with superior toughness, even at low temperature.

Because of its excellent impact strength- down to 0C°, and its improved creep rupture properties under internal pressure stress, ZR230C is well suited for production of pressure pipes for industry, heating pipes and under floor hot water heating, domestic service pipes (hot and cold water) and weldable fittings.

Application

Extrusion application of ZR230C include profiles, pipes and tough sheet for industrial applications. This grade is especially suitable for applications requiring high resistance to temperature, and aggressive media.

Tolerance

Method

Unit

Value

Properties

(+/-) 0.5

ASTM D 1238

gr/10 min

0.35

Melt flow rate(230 C°,2.16 kg)

(+/-) 0.2

ASTM D 1238

gr/10 min

1.7

Melt flow rate( 230C°,5.0 Kg)

(+/-) 5

ASTM D 1525

135

Vicat softening point(9.8 N)

(+/-) 8

ASTM D 648

75

H.D.T.(0.46 MPa)

(+/-) 120

ASTM D 790

MPa

1000

Flexural modulus

(+/-) 4

ASTM D 638

MPa

28

Tensile strength@ Yield

-2

ASTM D 638

%

15

Elongation@Yield

-

ASTM D 256

J/m

No Break

Izod impact strength(notched)@23 C°

(+/-)

ASTM D 256

J/m

50

Izod impact strength(notched)@

-20 C°

+10

ASTM D 758

R-B

75

Rockwell hardness

(R-B scale)


 

Value shown are average and are not to be considered as exact product specifications.*

            * All specimens are prepared by injection molding.

 

 

 

Commercial Manager cell phone: +98- 912 127 45 75

 