ABS-40

AKSAD GROUP PETROCHEM

ABS-40

 

Classification:

General Purpose

Characteristic:

High Impact Resistance

Application:

Automobile parts (radiator grill & etc.), Helmets, Toys, Suitcase, Shoe heels, skis, golf club heads, Sports equipment, suitcases, & etc.

 

ABS-40

specification

Typical Value

Unit

Test Condition

Test Method

(ASTM)

Properties

Min 26

32

Kj/m2

6.4 mm, notched

D-256

Izod impact

18-28

25

Gr/10min

220c° , 10g

D-1238

Melt flow index

90-110

98

R-scale

-

D-785

Rock well hardness

Min 82

82

1.82 m pa

D-648

HDT

Min 93

92

5kg/50 c°

D-1525

Vicat Softening Temp

Min 390

400

Kg/cm2

23 c° ,50 mm/min

D-638

Tensil strength

Min 25

30

%

23 c° , 50 mm/min

D-638

Tensil elongation

Min 530

580

Kg/cm2

23 c° , 2.8 mm/min

D-790

Flexural strength

Min 15000

18000

Kg/cm2

23 c° , 2.8 mm/min

D-790

Flexural Modulus

1.04

1.04

-

23 c°

D-792

Specific Gravity

0.4-0.7

0.4-0.7

%

-

D-955

Molding Shirinkage

HB

HB

-

1/8 inch(3.2mm)

UI94

Flammability


 

Typical ABS Processing Conditions:

Drying: It is recommended that ABS Resin be dried at (80-85 c°) for 3 hours.

The following molding conditions are recommended starting point for GBPC ABS Resin. A moisture level of ≤0.1 % should be reached before injection molding the resin.

Some modifications may be required depending on the specific molding equipment and part configuration.

 

INJECTION MOLDING

 

Melt Temp (°c)

Nozzle Temp (°c)

Front Temp (°c)

Center Temp (°c)

Center Temp (°c)

Rear Temp(°c)

230

215-225

210-220

210-220

200-210

190-200

 

 

 

 

Filling Speed

Mold Temp (°c)

 

 

 

 

Slow-Med

60-80


 

 

 

 

 

 

Commercial Manager cell phone: +98- 912 127 45 75

 