AKSAD GROUP PETROCHEM
HFI5110
PRODUCT DESCRIPTION
HFI5110 is a high molecular weight, high density polyethylene, which has a broad molecular weight distribution and high melt strength. This product specially designed for producing thin films with excellent strength and rigidity.
APPLICATIONS
HFI5110 is recommended for blown film extrusion. This product is suitable for manufacture of high strength grocery sacks, shopping bags and high quality thin films for uni/multi-wall packaging. Films produced withthis product can be readily treated and printed to give high quality graphi
PROPERTIES
Extruder temperature profile: 200-235°C
Frost line height: 6-8 times die diameter
Blow Up Ratio: 3-5
Recommended film thickness: 15 to 50 μm
Please note that, these processing conditions are recommended by producer only for 100% HFI5110 resin (not in the case of blending with any other compatible material), but because of the many particular factors
which are outside our knowledge and control, and may affect the use of product, no warranty is given
|
Method
|
Unit
|
Value
|
Properties
|
|
ISO 1183
|
kg/cm3
|
951
|
Density (23 oC)
|
|
ISO 1133
|
dg/min
|
10
|
MFI (190 oC /21.6Kg)
|
|
ISO527-1;2
|
MPa
|
1050
|
Tensile Modulus of elasticity
|
|
ISO 527-1;3
|
MPa
|
55
|
Tensile Strength (MD)
|
|
ISO 527-1;3
|
MPa
|
55
|
Tensile Strength (TD)
|
|
ISO 527-1
|
%
|
580
|
Tensile Strain at Break (MD)
|
|
ISO 527-1
|
%
|
620
|
Tensile Strain at Break (TD)
|
|
ISO 527-1
|
MPa
|
26
|
Tensile stress at Yield
|
|
ISO 527-1
|
%
|
10
|
Tensile strain at Yield
|
|
ISO 6383-2
|
mN
|
250
|
Elemendorf tear strength(MD)
|
|
ISO 6383-2
|
mN
|
800
|
Elemendorf tear strength(TD)
|
|
ISO 3146
|
C°
|
132
|
Melting Point
|
|
ISO 306
|
C°
|
127
|
Vicat Temperature , (A50,50 oC/h , 10N)
|
|
|
|
|
Additives :Antioxidant –Heat stabilizer Zinc Stearate
|